ASTM G48 – Download as PDF File .pdf), Text File .txt) or read online. Fig. 2 Example of pitting after corrosion testing in accordance with ASTM G48 Method A. The test temperature of 22 °C is too aggressive for lean duplex grades . The ASTM GA test (ferric chloride test) is widely used for pre-qualification of corrosion resistant alloys, welds and weld overlays for oil and gas industry.

Author: Gardasida Arazilkree
Country: India
Language: English (Spanish)
Genre: Travel
Published (Last): 3 August 2009
Pages: 400
PDF File Size: 7.27 Mb
ePub File Size: 8.82 Mb
ISBN: 511-4-78213-190-5
Downloads: 21014
Price: Free* [*Free Regsitration Required]
Uploader: Zulushakar

The Eng-Tips staff will check this out astm g48 take appropriate action. Perhaps not at temp long enough or not cooled quickly enough. Method C — Critical pitting temperature test for nickel-base and qstm alloys.

Historical Version s – view previous versions of standard. astm g48

This should indicate if you have any intermetallic phases present. Promoting, selling, recruiting, coursework and thesis posting is forbidden. In many ways, G is ideal for use instead of methods C-F as it is a more rapid method that can be performed within days instead of weeks. All sample surfaces must be freshly ground with no further treatment.

Overmatched filler etc astm g48 you have good micros and impacts then the test is probably just too severe. Other astm g48 are given in parentheses for information astm g48. Reasons such as off-topic, duplicates, flames, illegal, vulgar, or students posting their homework.

Corrosion Testing to ASTM G48 using Method A – Corrosion engineering – Eng-Tips

Methods D and F use a multiple crevice astm g48 which has a number of grooves and plateaus and is attached to the test sample with an insulated bolt. The specimen size is 1″ X 2″ cut at astm g48 and prepared only using grit abrasive paper and astm g48 not passivated or pickled. Unfortunately, if the client wants a 72 hour test, that is their prerogative. Share on Tumblr Print. When using stainless and duplex steels, ASTM G48 is widely used to ensure the quality of the material and resistance to pitting and crevice corrosion.

  AS431 DATASHEET PDF

Please advise, is it acceptable if we astm g48 submit TQ to client to lower the testing time to 24 hours instead of 72 hours for normal duplex wrought specimen because G48 is astm g48 on timings and suggests 72 hours although variations may also be used. It is the responsibility of the user of this standard to establish appropriate safety and astm g48 practices and determine the applicability of regulatory limitations prior to use. Close this window and log in.

The results may be used for ranking alloys in order of increasing resistance to pitting and crevice corrosion initiation under the specific conditions of these methods. You may polish the edges, if the finished product is pickled then you can pickle, the times and temps are general guidance.

The oil and gas industry has spent a great deal of time and effort since the 80s in arriving at a standardised G48 astm g48 for duplex. Resources Digital transformation may be the most frequently misunderstood and misused term in business discourse today. Posting Guidelines Promoting, astm g48, recruiting, coursework and thesis posting is forbidden. The sample was pickled and prepared but still could not astm g48 the client requirements no pitting or crevice corrosion in either weld metal or HAZ is permitted and failed in testing twice.

About us Contact us Astm g48 Terms of use. We hired an independant 3rd party to perform corrosion testing to G48 Method A as per client requirements but by mistake 3rd party booked the specimen to A and testing was done also to A and result is OK. No statement can be made about resistance of alloys in environments that do not contain chlorides.

Testing by ASTM G48 for Pitting and Crevice Corrosion

This is a simple immersion test astm g48 the test sample is placed in a temperature-controlled solution of FeCl 3. When testing as-welded, cylindrical, or astm g48 non-flat samples, the standard crevice formers will not provide uniform contact. Grinding or pickling on stainless steel surfaces may destroy the passive layer.

  HEAD FIRST EJB3.0 PDF

Method F — Critical crevice temperature test for stainless steels. Log in to your subscription Username. Don’t astm g48 mix and match with test conditions and procedures. You should ignore any edge corrosion If samples fail then they were not annealed correctly.

Secondly, have you done an A test? Methods A and B are designed to cause the breakdown of Type at room temperature.

Sheriff’s Encyclopedic Dictionary of Applied Geophysics, fourth edition. Which test do I need?

astm g48 Proceedings of an international conference Diverless and Deepwater Techology: Link to Active This link will always route to the current Active version of the standard. Exposure time shall be 24 hours.

G2MT Laboratories

The crevice former contact area of Method B is a A good suggestion earlier is to test the astm g48 metal this will demonstrate if you have any chance of passing. Client is not accepting the results and require to perform the testing to G48 Method A for 72 hours.

Are the specimens with or without PWHT? The acceptance criteria, no pitting or crevice corrosion either at weld metal or HAZ is permitted, is mentioned astm g48 in client specification.

Log in to your subscription

Astm g48 torque applied to the bolting assembly is 0. If testing protocol astm g48 the problem I would look at composition and solution treatment for answers. Red Flag This Post Please let us know here why this post is inappropriate.

The available pitting and crevice testing methods include:. The purpose of A is to detect intermetallic phases.